Abstract

A small but significant proportion of the archaeological iron objects in the British Museum collection have been problematic in that some of them have required repeated treatment. The deterioration of iron objects during storage was studied using microscopy, Raman spectroscopy, X-ray diffraction, scanning electron microscopy/energy dispersive X-ray analysis, X-ray fluorescence spectroscopy and ion chromatography. A total of 125 iron objects, including 56 from two British Roman sites and 69 from three Anglo-Saxon sites, were studied. Both surface corrosion and corrosion layers on polished cross-sections were investigated. The study revealed that the present condition of the iron objects varies; some are in a stable condition and others have been deteriorating, with pitting and weeping present on the surface. No treatment method had stopped corrosion for every object, although the alkaline sulphite treatment seemed to be more effective than the other methods. The results also showed that chloride ions can be present at the interface of the metal and inner corrosion layers. It is recommended that iron objects which have been mechanically cleaned without desalination treatments are kept in a dry environment to prevent further deterioration.

Cite this work

No public copy is stored for this record, so only the metadata is cited.

Stored only when both papers are in the corpus — 28 citations exist upstream.

Papers that cite the same references — the relational fallback while embeddings are still backfilling.