Eight sherds of ninth–tenth century ad Abbaesid blue‐and‐white glazed earthenware, excavated in 1931 at Hira in western Iraq, were analysed using, variously, quantitative wavelength‐dispersive spectrometry (WDS) and energy‐dispersive spectrometry (EDS) in association with scanning electron microscopes (SEM), and semi‐quantitative X‐ray fluorescence spectrometry (XRF). In order to compare the compositions of the cobalt pigments used, the glazes of seven complete vessels of eighth century ad Chinese Tang blue‐and‐white sancai were also analysed semi‐quantitatively using XRF. The Abbasid wares were shown to have used traditional Mesopotamian alkali–lime glazes applied to calcareous clay bodies. Half the glazes examined were opacified with tin oxide. Three types of blue decoration (i.e., raised; spreading; and flat, non‐spreading) were produced using a variety of formulations, including a mixture of cobalt pigment with lead oxide. The sources of the ores used for the cobalt pigments have not been identified. However, the analytical data showed that the cobalt ore used for the Abbasid blue‐and‐white ware could be distinguished from that used for the Tang blue‐and‐white sancai by its higher iron content and by the presence of a significant amount of zinc. The use of cobalt‐blue decoration on the ninth–tenth century ad Abbasid ware was anticipated in China by eighth century ad Tang blue‐and‐white sancai wares. However, whether its introduction by the Abbasid potters should be seen as an independent invention that followed the introduction of tin‐opacified glazes in Iraq, or whether it was influenced in some way by Chinese originals, is still unresolved.
Stored only when both papers are in the corpus — 46 citations exist upstream.